IMPACT OF MICRO AND MESOSTRUCTURE ON THE FAILURE RESISTANCE OF LASER POWDER BED FUSION-PROCESSED MATERIALS

IMPACT OF MICRO AND MESOSTRUCTURE ON THE FAILURE RESISTANCE OF LASER POWDER BED FUSION-PROCESSED MATERIALS

Bernd GludovatzGrand Ballroom E

Engineering materials processed using additive manufacturing (AM) techniques such as laser powder bed fusion (LPBF) often exhibit unique microstructures and defects that must be controlled to obtain peak performance in mechanical properties and as such a level of damage-tolerance that cannot be achieved in cast alloys. However, our understanding of how processing conditions control micro- and mesostructure and, in turn, mechanical performance, particularly regarding failure resistance, is weak. Furthermore, heat treatments that have been designed to achieve peak performance in cast alloys are often not optimized for alloys that have been processed using AM techniques. Here, we report our work on the effect of processing parameters such as layer thickness, hatch spacing, and scan strategy on crack resistance curve (R-curve) behavior in different orientations of LPBF-processed AlSi10Mg and correlate mechanical performance with meso- and microstructural features such as melt pool arrangement, cell morphology, grain size, grain orientation, and texture. Compared to that we show how heat-treatments impact fracture resistance as well as their anisotropy in two orthogonal orientations in an LPBF-processed 18Ni-300 maraging steel.
EXTENDED ABSTRACT

UNSW Sydney, Australia
Wed 10:30 - 10:50
Fatigue and Fracture of Additively Manufactured Materials 
Posted in .